Alloys
(UNS No.) |
Chemical
Composition
(%) |
Density
(g/cm) |
Mechanical Property(Normal Temperature) |
Specification |
| Condition |
Tensile
Strength
1000psi
(Mpa) |
Yield
Strength
1000psi
(Mpa)
at 0.2%
Offset |
Hardness
Brinell
(Rockwell) |
HASTELLOY
B-2
(N10665) |
Ni BAL Cr 1.0
Mo 28 Mn 1.0
Fe 2.0 Si 0.10
Co 1.0 C 0.01 |
9.22 |
Annealed |
132.5
(914) |
57.5
(396) |
228
(B-98) |
ASTM B(ASME SB-)333,335
619, 622, 626
AWS A5.14, A5.11 |
HASTELLOY
C-276
(N10276) |
Ni BAL W 4
Mo 16 Co 2.5
Cr 15.5 Mn 1.0
Fe 5.5 C 0.01 |
8.89 |
Annealed |
114.9
(792) |
51.6
(356) |
184
(B-90) |
ASTM B(ASME SB-)574,575
619, 622, 626
DIN 17744,17750,17751,17752, W.Nr.2.4819 |
HASTELLOY
C-4
(No6455) |
Ni BAL Co 2.0
Cr 16 Mn 1.0
Mo 15.5 Ti 0.7
Fe 3.0 C 0.01 |
8.64 |
Annealed |
116.2
(801) |
61.0
(421) |
194
(B-92) |
ASTM B(ASME SB-)574,575
619, 622, 626
AWS A5.14, A5.11 |
HASTELLOY
C-22
(N06022) |
Ni BAL
Cr 20-22.5
Mo 12.5-14.5
W 2.5-3.5
Co 2.5 C 0.01 |
8.69 |
Annealed |
116.3
(802) |
58.5
(403) |
184
(B-90) |
ASTM B(ASME SB-)574,575
619, 622, 626
AWS A5.14, A5.11 |
HASTELLOY
G
(N06007) |
Ni BAL Co 2.5
Cr 22 Cb+Ta 2
Fe 19.5 Cu 2
Mo 6.5 Mn 1.5
W 1 Si 1 |
8.30 |
Annealed |
102.0
(703) |
46.2
(319) |
161
(B-64) |
ASTM B(ASME SB-)581,582
619, 622, 626
AWS A5.14, A5.11 |
HASTELLOY
G-3
(N06985) |
Ni BAL Co5
Cr 21-23.5 Cu 1.5-2.5
Fe 18-21 W 1.5
Mo6-8 Si 1
Mn 1 C 0.015 |
8.30 |
Annealed |
99.0
(68.3) |
44.0
(303) |
158
(B-83) |
ASTM B(ASME SB-)581,582
619, 622, 626
AWS A5.14, A5.11 |
HASTELLOY
G-30
(N060630) |
Ni BAL Mo 5.0
Cr 29.5 W2.5
Fe 15.0 Mn 2.0
Cu 1.7 Co 5.0
Si 1.0 |
8.22 |
Annealed |
100
(690) |
47
(324) |
176
(B-88) |
ASTM B(ASME SB-):
CODE CASE 1979 |
HASTELLOY
X
(N06002) |
Ni BAL Co 1.5
Cr 22 Si 1
Fe 18.5 Mn1
Mo9 W 0.6
C 0.1 AI 0.5
Ti 0.15 |
8.22 |
Annealed |
109.5
(755) |
55.9
(385) |
194
(B-92) |
ASTM B(ASME SB-)435,572
619, 622, 626, AMS 5390, 5536,
AWS A5.14, A5.11 |
| |
|
|
|
|
|
|
|